N200 SILVER 200℃ Heat-Resistant Aluminum Silver Paint

Product Introduction:

This heat-resistant coating product is formulated with silicone resin as the main resin base and high-temperature resistant flake aluminum powder as a filler. The coating is designed to provide excellent thermal stability and weather resistance, and is suitable for surface protection in high-temperature environments.

characteristic:

1. Heat resistance: The coating can withstand high-temperature environments, providing excellent thermal stability and is suitable for long-term exposure to high temperatures (depending on formulation adjustments).

2. Corrosion resistance: The silicone resin matrix combined with flake aluminum powder provides an excellent barrier effect, resisting oxidation, chemical corrosion and environmental erosion.

3. Pigment compatibility: It is particularly suitable for use with metallic pigments (such as flake aluminum powder) to form a uniform metallic gloss coating and enhance the aesthetics.

4. Stability and ease of application: The solvent-based formula has high storage stability; it can be applied by spraying or brushing, and after baking and curing, it forms a smooth and wear-resistant surface.

5. Environmentally friendly and compliant: Low volatile organic compound (VOC) content, meeting industrial coating environmental standards.

use:

1. Steel structure surface protection: mainly used for surface coating of steel frames, bridges and building structures, providing a heat-resistant and corrosion-resistant layer to extend service life.

2. Industrial equipment coating: Colored baking enamel paint suitable for high-temperature components such as space heaters, stoves, exhaust systems and heat exchangers.

3. Maintenance and decorative coatings: Used for maintenance coatings on metal substrates, combined with metal pigments to achieve decorative effects, suitable for chemical plants, power plants and oil refining equipment.

4. High-temperature protective coating: When exposed to high temperatures, humidity or chemical media, it acts as a protective topcoat to prevent substrate oxidation and thermal degradation.

Product characteristics:

Viscosity: 60 ± 5 KU (25℃)

Specific gravity (g/ml): 1.29 ± 0.05 (g/ml)

Volumetric solids (%): 36 ± 1%

Flash point: 24°C

Color: Silver

Thinner kit: NPS-100/DR-400
Thinner dosage: (excluding tool cleaning)

Construction method	Airless spray	Air spray	Brush paint	Rolling
Amount added (%)	5-10%	5-10%	5-10%	5-10%

Application methods: airless spraying, air spraying, brushing, rolling.

Recommended number of coats: 1

Drying time:

Min (minutes), H (hours), D (days)	30°C
Touch time	1/3H
Hardening time	8H
Repaint interval (lowest)	10H

Drying time will vary depending on the ambient temperature and humidity.

Theoretical coverage:

Typical: 14.4 m²/L/coat (dry film thickness: 25 μm (per coat))
It is recommended that the coating thickness be at least three times the maximum roughness (Rz) to achieve a good protective effect.

Instructions for use:

Surface treatment requirements:

Use a solvent to remove visible grease, oil, lubricants, cutting fluid, and other soluble contaminants from the metal surface that may affect adhesion, or use other methods to prepare the surface condition for the coating application, following the SSPC-SP1 surface treatment standard to prepare for subsequent protective coating applications.

The steel structure surface must be sandblasted to Sa2.5 (very thorough sandblasting) or SSPC-SP10 grade. Without using a magnifying glass, at least 95% of the surface area should be free of any visible oil, grease, dust, dirt, scale, rust, coatings, oxides, corrosion products, and other foreign matter. The surface roughness should be in the range of Rz 30-75μm.

Power tool treatment must meet St 3. This standard defines the use of power tools (such as power wire brushes, grinders, abrasive discs, etc.) to remove loose rust, scale, old coatings, and other foreign matter from steel surfaces until the surface has a metallic sheen. However, minor scratches and discoloration are permissible. It is equivalent to SSPC-SP3 in the US SSPC standard.

Surface defect treatment: This includes weld slag, burrs, cracks, and holes. These defects affect the adhesion and protective effect of the coating and should be removed or repaired as much as possible.

After surface treatment, a thorough inspection should be conducted to ensure that there are no contaminants or defects such as oil, grease, dust, dirt, scale, rust, welding slag, or burrs before proceeding with the next step.

Under any atmospheric conditions, it is best to perform the coating work within 1 hour after the completion of the "surface treatment" procedure, and no later than 8 hours after the "surface treatment".

Different coatings have different requirements for surface cleanliness and roughness. Please discuss this in detail with our sales staff before using this product.

Construction environment requirements:

Coating application should be carried out under suitable environmental conditions to ensure the quality of the coating. The following factors should be considered:

Temperature: Please construct within the recommended temperature range. Generally, it is not advisable to construct in environments below 5℃ or above 40℃.

Humidity: Relative humidity should not exceed 85%. Avoid construction in humid or rainy weather.

Wind speed: Excessive wind speed will affect the spraying effect; avoid construction on windy days.

Surface temperature: The surface temperature of the steel should be at least 3°C ​​higher than the dew point temperature to avoid condensation on the surface.

Storage:

Storage validity period: 2 years

This product must be stored in a cool, dry, and well-ventilated place, away from direct sunlight and fire.

Notes:

Please read the paint instructions carefully before application.

The paint should be thoroughly stirred after opening the can.

Strictly follow the dilution ratio specified in the instructions; do not dilute excessively.

Please mix the main agent and hardener thoroughly according to the proportions indicated in the instruction manual.

This product is flammable and should be kept away from heat sources and open flames.

The work area should be well-ventilated during construction, and workers should avoid contact with skin and eyes. Please refer to SDS for relevant information.

Unused main agent and hardener should be sealed separately and stored in a cool place.

Packaging specifications:

Supporting specifications:	18.0	L
Supporting specifications:	3.6	L

Safety Precautions:

1. Ensure good ventilation during application, and keep the paint away from direct sunlight and heat sources.
2. To avoid skin and eye contact or inhalation of excessive paint fumes, please use protective equipment such as a face mask and gloves.
3. If it gets into your eyes, rinse immediately with plenty of water and seek medical attention.
4. Keep out of reach of children.

Disclaimer:

The above information represents typical properties, characteristics, and applications of the product and is intended only as guidance from our company. It should not be considered a warranty, a statement requiring the company to assume legal liability, or a basis for presuming the company to be liable. Users are responsible for confirming the suitability of any batch of product for a specific application before using the information and content presented in this manual.