Heat Shrink Neoprene Tube
Made of cross linked chlorinated polyolefin. Resistant to most fluids and solvents, including aviation and ground-vehicle fuels, lubricating oil, and hydraulic fluids. Good flexibility at low temperature. Resistant to abrasion and physical abuse while providing flexibility and strain
| Property | Test Method | Standard Value |
| Tensile Strength | ASTM D 412 | ≥10.3MPa |
| Elongation at Break | ASTM D 412 | ≥225% |
| Tensile Strength at 200% elongation | ASTM D 412 | ≤10.3MPa |
| Tensile Strength After Aging (120℃, 168hrs) | SAE-AMS-DTL-23053 | ≥8.3MPa |
| Elongation at Break After Aging（120℃，168hrs） | SAE-AMS-DTL-23053 | ≥175% |
| Dielectric Strength | ASTM D 2671 | ≥11.8kV/mm |
| Volume Resistivity | ASTM D 876 | ≥1x10 11 Ω.cm |
| Flammability (Self extinguishing 15 seconds; 3 inches) | ASTM D2671, Procedure A | Pass |
| Fungus resistance | ASTM G 21 | No growth |
| Low temperature flexibility | -70℃, 4 hrs |
No cracking |
| Product No. | As Supplied /mm | Recovered/mm | |
| Inner Diameter | Wall thicknes | ||
| WRSLD-3.2/1.5 | ≥3.2 | ≤1.5 | 0.7±0.2 |
| WRSLD-4.8/2.5 | ≥4.8 | ≤2.5 | 0.8±0.2 |
| WRSLD-6.4/3.4 | ≥6.4 | ≤3.4 | 0.9±0.2 |
| WRSLD-9.5/5.4 | ≥9.5 | ≤5.4 | 1.0±0.2 |
| WRSLD-12.7/7.1 | ≥12.7 | ≤7.1 | 1.2±0.3 |
| WRSLD-16/8.7 | ≥16 | ≤8.7 | 1.3±0.3 |
| WRSLD-19.1/10.5 | ≥19.1 | ≤10.5 | 1.4±0.3 |
| WRSLD-22.2/12.5 | ≥22.2 | ≤12.5 | 1.7±0.3 |
| WRSLD-25.4/14.5 | ≥25.4 | ≤14.5 | 1.8±0.3 |
| WRSLD-31.8/18.0 | ≥31.8 | ≤18.0 | 2.2±0.3 |
| WRSLD-38.1/21.5 | ≥38.1 | ≤21.5 | 2.4±0.3 |
| WRSLD-44.5/24 | ≥44.5 | ≤24.0 | 2.4±0.3 |
**Wall thickness will be less when shrinkage is restricted.