RSFR-(2X)125G(CB) - Ultra-thin Flame-retardant Heat Shrink Tubing
RSFR-(2X)125G(CB) - Ultra-thin Flame-retardant Heat Shrink Tubing
Couldn't load pickup availability
Application areas:
Protection of electronic, communication, and automotive parts, etc.
Product Description
Compliance standards: UL224 , CAN/CSA C22.2 NO198.1-99
Heat shrink ratio: 2:1
Initial shrinkage temperature: ≥ +70 ℃
Complete shrinkage temperature: ≥ +110 ℃
Operating temperature: -55 ℃ ~ +125 ℃
Flame retardant , environmentally friendly, and fast shrinkage.
Environmental Standards: RoHS
Standard colors: ten international standard colors including black, white, red, yellow, green, and blue .
Product Parameters
|
performance |
index |
Test methods |
|
Tensile strength |
≥10.4 MPa |
ASTM D 2671 |
|
Elongation at break |
≥200% |
ASTM D 2671 |
|
Tensile strength after aging |
≥7.3 MPa |
158 ℃ × 168h |
|
Elongation at break after aging |
≥100% |
158 ℃ × 168h |
|
Axial change rate |
-5% to +5% |
ASTM D 2671 |
|
Flame retardancy |
VW-1 |
ASTM D 2671 C method |
|
Withstand voltage (300V) |
1500 V , no breakdown in 1 minute |
UL224 |
|
Breakdown strength ( either breakdown strength or withstand voltage ) |
≥15kV/mm |
ASTM D 149 |
|
Volume resistivity |
≥10 14 Ω·cm |
IEC 60093 |
Product Selection
|
Specification |
Supply inner diameter (mm) |
Fully shrunk dimensions (mm) |
Standard packaging Rice / plate |
Scope of application (mm) |
|
|
inner diameter |
Wall thickness |
||||
|
0.90±0.20 |
≤0.40 |
0.20±0.10 |
200 |
0.4~0.7 |
|
|
Φ0.8CB |
1.10±0.20 |
≤0.50 |
0.20±0.10 |
200 |
0.6~0.8 |
|
Φ1.0CB |
1.40±0.20 |
≤0.65 |
0.20±0.10 |
200 |
0.7~1.0 |
|
Φ1.5CB |
1.90±0.20 |
≤0.85 |
0.20±0.10 |
200 |
0.9~1.4 |
|
Φ2.0CB |
2.40±0.20 |
≤1.00 |
0.22±0.10 |
200 |
1.1~1.8 |
|
Φ2.5CB |
2.90±0.20 |
≤1.30 |
0.25±0.10 |
200 |
1.4~2.3 |
|
Φ3.0CB |
3.40±0.20 |
≤1.50 |
0.28±0.10 |
200 |
1.6~2.7 |
|
Φ3.5CB |
3.90±0.20 |
≤1.80 |
0.28±0.10 |
200 |
1.9~3.2 |
|
Φ4.0CB |
4.40±0.20 |
≤2.00 |
0.30±0.10 |
200 |
2.1~3.6 |
|
Φ4.5CB |
4.90±0.20 |
≤2.30 |
0.30±0.10 |
200 |
2.4~4.0 |
|
Φ5.0CB |
5.50±0.20 |
≤2.50 |
0.32±0.10 |
100 |
2.6~4.5 |
|
Φ6.0CB |
6.50±0.20 |
≤3.00 |
0.32±0.10 |
100 |
3.1~5.4 |
|
Φ7.0CB |
7.50±0.30 |
≤3.50 |
0.32±0.10 |
100 |
3.7~6.3 |
|
Φ8.0CB |
8.50±0.30 |
≤4.00 |
0.32±0.10 |
100 |
4.2~7.2 |
|
Φ9.0CB |
9.50±0.30 |
≤4.50 |
0.35±0.10 |
100 |
4.7~8.0 |
|
Φ10CB |
10.50±0.30 |
≤5.00 |
0.35±0.10 |
100 |
5.2~9.0 |
|
Φ11CB |
11.50±0.30 |
≤5.50 |
0.40±0.10 |
100 |
5.7~10.0 |
|
Φ12CB |
12.50±0.30 |
≤6.00 |
0.40±0.10 |
100 |
6.2~11.0 |
|
Φ13CB |
13.50±0.30 |
≤6.50 |
0.40±0.10 |
100 |
6.7~12.0 |
|
Φ14CB |
14.50±0.30 |
≤7.00 |
0.40±0.10 |
100 |
7.3~13.0 |
|
Φ15CB |
15.50±0.40 |
≤7.50 |
0.40±0.10 |
100 |
7.8~14.0 |
|
Φ16CB |
16.50±0.40 |
≤8.00 |
0.40±0.10 |
100 |
8.3~15.8 |
|
Φ17CB |
17.50±0.40 |
≤8.50 |
0.40±0.10 |
100 |
8.8~16.0 |
|
Φ18CB |
18.50±0.40 |
≤9.00 |
0.42±0.10 |
100 |
9.3~17.0 |
|
Φ20CB |
20.50±0.50 |
≤10.0 |
0.45±0.10 |
100 |
10.5~19.0 |
|
Φ22CB |
22.50±0.50 |
≤11.0 |
0.45±0.10 |
100 |
11.5~20.5 |
|
Φ25CB |
25.50±0.50 |
≤12.5 |
0.45±0.10 |
100 |
13.0~24.0 |
|
Φ28CB |
28.50±0.50 |
≤14.0 |
0.45±0.10 |
100 |
14.5~27.0 |