RSFR-(2X)125HCX - Magnetic Sleeve
RSFR-(2X)125HCX - Magnetic Sleeve
Couldn't load pickup availability
Application areas:
Electronic components
Product Description
Heat shrink ratio: 2:1
Soft and non-flame retardant
Initial shrinkage temperature: ≥+84 ℃
Complete shrinkage temperature: ≥+120 ℃
Operating temperature: -55 ℃ ~ +125 ℃
Superior electromagnetic compatibility
Environmental Standards: RoHS
Standard color: Black
Product Parameters
|
project |
Performance indicators |
Test Standards |
|
|
Tensile strength |
≥10.4 MPa |
GB/T1040 |
|
|
Elongation at break |
≥200% |
||
|
Tensile strength after aging |
≥7.3 MPa |
UL224 (158°C × 168h) |
|
|
Elongation at break after aging |
≥100% |
||
|
Heart rate |
≥70% |
UL224 |
|
|
cold bending |
No cracking |
UL224 (-30 ℃ ×1h) |
|
|
density |
≤2.5 g/ cm³ |
—— |
|
|
Water absorption rate |
≤0.5% |
ASTM D 570 |
|
|
chemical properties |
copper stability |
pass |
UL224 (158 ℃ × 168h) |
|
Corrosion resistance |
pass |
||
|
Electrical performance |
copper volume resistivity |
≥1×10 12 Ω·cm |
GB/T1410 |
|
Insulation withstand voltage |
1500V , no breakdown in 1 minute |
UL224 |
|
|
Operating frequency |
1K~500KHz |
—— |
|
|
Inductance rise |
≥10% |
—— |
|
Product Selection
|
Specification |
Supply inner diameter (mm) |
Fully shrunk dimensions (mm) |
Standard packaging Rice / plate |
|
|
Inside path |
wall thick |
|||
|
Φ4.0 |
4.70±0.40 |
≤2.0 |
0.45±0.10 |
200 |
|
Φ5.0 |
5.50±0.40 |
≤2.5 |
0.55±0.10 |
100 |
|
Φ6.0 |
6.50±0.40 |
≤3.0 |
0.55±0.10 |
100 |
|
Φ8.0 |
8.50±0.50 |
≤4.0 |
0.60±0.10 |
100 |
|
Φ10 |
10.50±0.50 |
≤5.0 |
0.60±0.10 |
100 |
|
Φ12 |
12.50±0.50 |
≤6.0 |
0.60±0.10 |
100 |
|
Φ14 |
14.50±0.50 |
≤7.0 |
0.65±0.10 |
100 |
Note : Sleeves smaller than Φ4 or larger than Φ14 are non-standard and will be manufactured according to order requirements.