RSFR-(2X)125HEC - Halogen-free flame-retardant polyolefin heat shrink tubing for batteries and capacitors
RSFR-(2X)125HEC - Halogen-free flame-retardant polyolefin heat shrink tubing for batteries and capacitors
Couldn't load pickup availability
Application areas:
Batteries and capacitors
Product Description
The halogen-free flame-retardant heat shrink tubing for batteries and capacitors is made of radiation-crosslinked polyolefin material. It has excellent physical, chemical and electrical properties, ultra-thin walls, high hardness, and is easy to insert. It is mainly used in batteries and capacitors to provide insulation and protection, and can completely replace PVC and PET tubing.
Heat shrink ratio: 2:1
Initial shrinkage temperature: ≥ +70 ℃
Complete shrinkage temperature: ≥+120 ℃
Operating temperature: -55 ℃ ~ +125 ℃
Halogen -free, flame-retardant, low-smoke, non-toxic, thin-walled, and fast-shrinking.
Environmental standards : RoHS , SONY
Standard color: Black (other colors can be customized)
Product Parameters
|
performance |
index |
Test Standards |
|
Tensile strength |
≥10.4 MPa |
ASTM D 2671 |
|
Elongation at break |
≥200% |
|
|
Tensile strength after aging |
≥7.3 MPa |
ASTM D 2671 (158 ℃ × 168h) |
|
Elongation at break after aging |
≥100% |
|
|
Axial change rate |
-5 % ~+5% |
ASTM D 2671 |
|
Flame retardancy |
VW-1 |
ASTM D 2671 B method |
|
Insulation withstand voltage ( 600V ) |
2500V , no breakdown in 1 minute |
UL224 |
|
Breakdown strength ( either breakdown strength or withstand voltage ) |
≥ 15kV/mm |
ASTM D 149 |
|
Volume resistivity |
≥10 14 Ω·cm |
IEC 60093 |
Product Selection
|
Specification |
Supply inner diameter (mm) |
Fully shrunk dimensions (mm) |
Standard packaging Rice / plate |
|
|
inner diameter |
Wall thickness |
|||
|
Φ5.0 |
5.50±0.20 |
≤2.5 |
0.32±0.10 |
100 |
|
Φ6.0 |
6.50±0.20 |
≤3.0 |
0.32±0.10 |
100 |
|
Φ8 |
8.50±0.30 |
≤4.0 |
0.32±0.10 |
100 |
|
Φ10 |
10.50±0.30 |
≤5.0 |
0.35±0.10 |
100 |
|
Φ12 |
12.50±0.30 |
≤6.0 |
0.35±0.10 |
100 |
|
Φ14 |
14.50±0.30 |
≤7.0 |
0.36±0.10 |
100 |
|
Φ16 |
12.50±0.30 |
≤8.0 |
0.36±0.10 |
100 |
|
Φ18 |
18.50±0.30 |
≤9.0 |
0.36±0.10 |
100 |
|
Φ20 |
20.50±0.40 |
≤10.0 |
0.40±0.10 |
100 |
|
Φ22 |
22.50±0.40 |
≤11.0 |
0.40±0.10 |
100 |
|
Φ25 |
25.60±0.40 |
≤12.5 |
0.40±0.10 |
50 |
|
Φ30 |
31.30±0.80 |
≤17.6 |
0.43±0.10 |
50 |
|
Φ35 |
36.30±0.80 |
≤20.5 |
0.48±0.10 |
50 |
|
Φ40 |
41.30±0.80 |
≤23.5 |
0.65±0.10 |
50 |
|
Φ45 |
46.30±0.80 |
≤26.4 |
0.65±0.10 |
25 |
|
Φ50 |
51.30±0.80 |
≤29.4 |
0.65±0.10 |
25 |
|
Φ55 |
56.50±1.00 |
≤32.3 |
0.65±0.10 |
25 |
|
Φ60 |
61.50±1.00 |
≤35.2 |
0.65±0.10 |
25 |
|
Φ65 |
66.50±1.00 |
≤38.2 |
0.72±0.15 |
25 |
|
Φ70 |
71.50±1.00 |
≤41.1 |
0.72±0.15 |
25 |
|
Φ75 |
76.50±1.00 |
≤44.1 |
0.72±0.15 |
25 |
|
Φ80 |
81.50±1.50 |
≤47.0 |
0.72±0.15 |
25 |
|
Φ85 |
86.50±1.50 |
≤50.0 |
0.74±0.15 |
25 |
|
Φ90 |
92.00±1.50 |
≤52.9 |
0.74±0.15 |
25 |
|
Φ100 |
102.00±2.00 |
≤58.8 |
0.74±0.20 |
25 |
Note: The conditions for complete shrinkage are 200 ℃ for 3 min .