RSFRM—Flame-retardant middle-wall tube
RSFRM—Flame-retardant middle-wall tube
Couldn't load pickup availability
Application areas:
Product Description
Heat shrink ratio: 3:1
Initial shrinkage temperature: ≥ +70 ℃
Complete shrinkage temperature: ≥ +125 ℃
Operating temperature: -45 ℃ ~ +125 ℃
UV protection
Environmental Standards: RoHS
Standard color: Black (other colors can be customized)
Product Parameters
|
performance |
index |
Test methods |
|
Tensile strength |
≥10.4 MPa |
ASTM D 2671 |
|
Elongation at break |
≥200% |
ASTM D 2671 |
|
Strength after heat aging |
≥7.3 MPa |
158 ℃ × 168h |
|
Elongation at break after heat aging |
≥100% |
158 ℃ × 168h |
|
Axial change rate |
-8% to +8% |
ASTM D 2671 |
|
Flame retardancy |
pass |
ASTM D 2671 Method B |
|
Breakdown strength |
≥15kV/mm |
IEC 60243 |
|
Volume resistivity |
≥10 14 Ω·cm |
IEC 60093 |
Product Selection
|
Specification |
Supply inner diameter (mm) |
Fully shrunk dimensions (mm) |
Standard packaging |
|
|
inner diameter |
Wall thickness |
|||
|
Φ6.0/2.0 |
≥6.0 |
≤2.0 |
1.80 ± 0.30 |
1.22 |
|
Φ10.2/3.0 |
≥10.2 |
≤3.0 |
1.75 ± 0.30 |
1.22 |
|
Φ16/5.0 |
≥16.0 |
≤5.0 |
1.90 ± 0.30 |
1.22 |
|
Φ19.1/5.6 |
≥19.1 |
≤5.6 |
2.45 ± 0.40 |
1.22 |
|
Φ25/8 |
≥25.0 |
≤8.0 |
2.45 ± 0.40 |
1.22 |
|
Φ28/9 |
≥28.0 |
≤9.0 |
2.60 ± 0.40 |
1.22 |
|
Φ35/10.2 |
≥35.0 |
≤10.2 |
2.70 ± 0.45 |
1.22 |
|
Φ38.1/12 |
≥38.1 |
≤12.0 |
2.70 ± 0.45 |
1.22 |
|
Φ43.2/12.7 |
≥43.2 |
≤12.7 |
2.70 ± 0.45 |
1.22 |
|
Φ52.1/16 |
≥52.1 |
≤16.0 |
2.80 ± 0.45 |
1.22 |
|
Φ63/19 |
≥63.0 |
≤19.0 |
2.80 ± 0.45 |
1.22 |
|
Φ75/22 |
≥75.0 |
≤22.0 |
3.00 ± 0.45 |
1.22 |
|
Φ85/25 |
≥85.0 |
≤25.0 |
3.00 ± 0.45 |
1.22 |
|
Φ95/29 |
≥95.0 |
≤29.0 |
3.30 ± 0.50 |
1.22 |
|
Φ115/34 |
≥115 |
≤34.0 |
3.70 ± 0.50 |
1.22 |
|
Φ125/36 |
≥125 |
≤36.0 |
3.70 ± 0.50 |
1.22 |
|
Φ130/36 |
≥130 |
≤36.0 |
3.70 ± 0.50 |
1.22 |
|
Φ140/42 |
≥140 |
≤42.0 |
3.70 ± 0.50 |
1.22 |
dd