RSFR-VDF150 - Flexible, High-Transparency, Flame-Retardant Heat Shrink Tubing
RSFR-VDF150 - Flexible, High-Transparency, Flame-Retardant Heat Shrink Tubing
Couldn't load pickup availability
Application areas:
It is widely used in motor wiring harness protection, temperature probes and other applications requiring long-term high-temperature operation.
Product Description
This flexible, highly transparent, flame-retardant heat shrink tubing is a thin-walled, high-temperature resistant heat shrink tubing with excellent transparency. It is made of flexible, chemically resistant, and high-temperature resistant modified fluoroplastics. It can be used to protect cables and cable markings from damage, effectively preventing mechanical damage and chemical corrosion. Its high transparency ensures that internal information is legible, protecting electronic components and maintaining their long-term identifiability. It is widely used in motor wiring harness protection, temperature probes, and other applications requiring long-term high-temperature operation.
Features:
Implementation standard: Meets SAE-ASM-DTL-23053/18 Class 2
Heat shrink ratio: 2:1
Initial shrinkage temperature: ≥+100 ℃
Complete shrinkage temperature: ≥+135 ℃
Operating temperature: -55 ℃ ~ +150 ℃
Highly flexible, does not wrinkle, excellent transparency, and lightweight.
Environmental standards : RoHS , REACH
Standard color: Transparent (other colors can be customized)
Product Parameters
|
performance |
index |
Test methods |
|
|
Physical properties |
size |
According to customer needs |
ASTM D 2671 |
|
Longitudinal length variation |
-10% to +5% |
ASTM D 2671 |
|
|
Tensile strength |
≥24.1 MPa |
ASTM D 2671 |
|
|
Elongation at break |
≥300% |
ASTM D 2671 |
|
|
Wall deviation rate |
≤40% |
AMS-DTL-23053 |
|
|
secant modulus |
≥172 MPa |
ASTM D 2671 |
|
|
density |
≤1.9 g/ cm³ |
ASTM D 2671 |
|
|
Low temperature flexibility |
No cracks |
AMS-DTL-23053 (-55 ℃ × 4h) |
|
|
thermal shock |
No dripping, no flowing, no cracking |
ASTM D 2671 (250 °C × 4h) |
|
|
Tensile strength after heat aging |
≥19.1 MPa |
ASTM D 2671 (225 °C × 168h) |
|
|
Elongation at break after heat aging |
≥200% |
ASTM D 2671 (225 °C × 168h) |
|
|
Transparency stability |
Identifiable internal markings |
AMS-DTL-23053 (200 ℃ × 24h) |
|
|
Electrical insulation performance |
Dielectric strength |
≥15.7kV/mm |
ASTM D 2671 |
|
Volume resistivity |
≥10 12 Ω·cm |
ASTM D 2671 |
|
|
Chemical properties |
Copper corrosion |
Non-corrosive |
ASTM D 2671 (160 ℃ × 16h) |
|
Flame retardant |
Self-extinguishing within 60 seconds , with the paper flag burned to less than 25% damage. |
UL224 VW- 1 ASTM D 2671 C method |
|
|
Water absorption rate |
≤0.5% |
ISO 846 B method , 23 ℃ × 24h |
|
|
Tensile strength after mold resistance |
≥24.1 MPa |
ASTM D 2671 |
|
|
Elongation at break after mold resistance |
≥300% |
ASTM D 2671 |
|
|
Dielectric strength after mold resistance |
≥15.7kV/mm |
ASTM D 2671 |
|
|
Tensile strength after chemical resistance |
≥13.8 MPa |
ASTM D 2671 |
|
|
Elongation at break after chemical resistance |
≥200% |
ASTM D 2671 |
|
|
Dielectric strength after chemical resistance |
≥15.7kV/mm |
ASTM D 2671 |
Product Selection
|
Specification |
Supply inner diameter (mm) |
Fully shrunk dimensions (mm) |
||
|
Imperial |
Metric |
inner diameter |
Single layer wall thickness |
|
|
3/64 |
Φ1.2 |
≥1.2 |
≤0.6 |
0.25±0.05 |
|
1/16 |
Φ1.6 |
≥1.6 |
≤0.8 |
0.25±0.05 |
|
3/32 |
Φ2.4 |
≥2.4 |
≤1.2 |
0.25±0.05 |
|
1/8 |
Φ3.2 |
≥3.2 |
≤1.6 |
0.25±0.05 |
|
3/16 |
Φ4.8 |
≥4.8 |
≤2.4 |
0.25±0.05 |
|
1/4 |
Φ6.4 |
≥6.4 |
≤3.2 |
0.30±0.08 |
|
3/8 |
Φ9.5 |
≥9.5 |
≤4.8 |
0.30±0.08 |
|
1/2 |
Φ12.7 |
≥12.7 |
≤6.4 |
0.30±0.08 |
|
3/4 |
Φ19.1 |
≥19.1 |
≤9.5 |
0.43±0.08 |
|
1 |
Φ25.4 |
≥25.4 |
≤12.7 |
0.48±0.08 |